Resin | Hardener | |
Mixing ratio (Parts by weight) | 100 | 12 |
Mixing ratio (Parts by volume) | 7.0 | 1 |
Viscosity | approx. 25,000 mPas | approx. 40 mPas |
Viscosity of the mixture | approx. 9,000 mPas | |
Mixed density | 1.45 kg/l | |
Bookfield RVT pot life, +23°C | 4 – 30 min (adjustable) | |
Curing time | 3 – 24 hrs. | |
Flash point | > 200°C | > 200°C |
Application instructions | The surfaces to be cast must be dry and clean. Tools for the production of shaped parts must be provided with a suitable release agent. The application is preferably carried out by casting with two-component dosing systems or by hand casting. PYRO-SAFE® B PX 2200 is insensitive to moisture and largely resistant to common technical oils and mild/diluted acids and alkalis. | |
Application (min. +5°C / < 90 % relative humidity) | For manual casting, the processing time at +23°C is between 4 – 30 min. The curing time is 3 – 24 hours. The pot and curing times are adjustable and depend on the temperature. | |
Storage | Dry, indoors. | |
Safety information | PYRO-SAFE® B PX 2200 is fibre- and solvent-free, non-toxic and not subject to any dangerous goods class. Further information can be found in the safety data sheet. |
Back
PYRO-SAFE® B PX 2200
Two-Component Casting Resin
PYRO-SAFE® B PX 2200 is a black intumescent two-component polyurethane-based casting resin. It is suitable for the production of cable penetration seals, elastic panels and shaped parts for preventive fire protection.
Field of Application
- Cable management
- On request
Downloads
Datasheets
Technical Data Sheet PYRO-SAFE® B PX 2200Technical Data
Moulding Material
Shore hardness (DIN 53505) | 88 – 93 Shore A; 45 – 50 Shore D |
Inflation pressure (300°C) method A, Sample thickness 5 mm, Ø 70 mm (DIBT Guidelines, 1996) | 0.6 – 1.2 N/mm² |
Foaming (450°C) | 17 to 26-fold |
Application temperature range | -50°C to +80°C |
Delivery & Packaging
Packaging | Tin | Cartridge | |
Container size | 1 kg | 5 kg | 200 ml |
Article number | on request |